20mm metal D Ring Buckle in light gold color

This is a customer-customized 20mm metal D ring buckle with engraved logo on both sides. It combines practicality and aesthetics. Due to its moderate size, sturdy and durable features, and customizable diverse colors, it is suitable for many types of bags.

Key attributes

Item	Metal D Ring Buckle	Size	20mm
Color	Light gold	Code	OYC0523
Material	Zinc alloy	Feature	Eco-Friendly, Durable,hight quality
Brand	SENNES	Packing	PP bag

Advantages of engraved logo on both sides of the zinc alloy D Ring buckle

Strengthening of brand identity

The logo is engraved on both sides of the d ring buckle, which looks neater visually and enhances brand recognition. compared with laser and printing, the logo is less likely to fall off and is clearer

Durability remains unchanged

The hardness of zinc alloy is moderate, the engraved position is not prone to deformation or fracture, will not damage the structure of zinc alloy, and will not affect the load-bearing performance of the d ring buckle

Enhance product differentiation

Logos and patterns can be customized according to customer requirements. the engraved characters on both sides are more symmetrical and exquisite, meeting the detailed requirements of high-end luggage

Optimize the visual aesthetics

Engraving can enhance the layering and three-dimensional effect of the d ring buckle, breaking the monotony of the metal surface

The causes of the problems that occurred during the quality inspection process of D Ring buckle

Unevenness defects appeared after electroplating

• The raw materials themselves have flaws, such as pores, shrinkage cavities and pockmarks
• The raw materials were not ground thoroughly, with burrs and scratches on the edges, which cannot be completely removed by polishing
• The surface cleaning steps of raw materials were not in place, resulting in uneven adhesion of the coating and local unevenness
• Parameter deviations during the electroplating process can lead to uneven deposition of the coating, directly causing surface unevenness.

The surface of the D buckle is peeling and rusting

• The adhesion between the coating and the substrate is insufficient
• The coating has defects such as damage or sand holes, and moisture or corrosive media enter, causing rust
• The zinc alloy material undergoes a chemical reaction, causing rust

a stamp on the top of the D Ring Buckle

• The current concentration at the contact point of the hanger causes the coating to be too thick or protruding, and the shape of the mark is consistent with the contact area of the hanger
• The hanging gear is damaged by contact and friction with the product. After electroplating, it cannot be covered and even the base is exposed